韩恩厚
,
韩玉梅
,
郑宇礼
,
柯伟
金属学报
在理论分析裂尖局部应变、应变速率及溶解速度的基础上、实验测定了低合金钢ZG20SiMn,SM50B—Zc的腐蚀疲劳裂纹扩展速率,并随着裂纹的扩展测定了裂纹内和裂纹尖端的pH值和金属电极电位、指出降低频率和增加应力比所导致的腐蚀疲劳裂纹扩展速率的增加部分主要来自于氢脆的加速作用
关键词:
腐蚀疲劳
,
stress ratio
,
frequency
,
crack growth
,
steel ZG20SiMn steel SM50B-Zc
,
null
汤忖江
,
尚成嘉
,
关海龙
,
王学敏
材料研究学报
doi:10.11901/1005.3093.2015.696
采用TMCP工艺获得了5种不同贝氏体体积分数的铁素体/贝氏体(F/B)多相钢.通过纵向力学性能分析,并结合修正C-J分析方法研究了以F/B多相组织为特征的大变形管线钢的应变硬化行为,获得了F/B多相钢中贝氏体体积分数与应力比、屈强比的关系,并通过修正C-J分析对此现象的机理进行了合理的阐释.结果表明,大变形管线钢的弹性形变阶段主要对应修正C-J分析中的第Ⅰ阶段,塑性形变阶段包括修正C-J分析第Ⅱ和第Ⅲ阶段,屈服点(应变0.5％)附近阶段可跨越第Ⅰ和第Ⅱ阶段.F/B多相钢中各阶段的应变硬化能力存在显著差异,并且其应变硬化行为呈现出与贝氏体体积分数相关的特性.通过适宜的组织调控可以实现管线钢强度和塑性的最佳匹配.应力比Rt1.5/Rt05适宜用于表征管材屈服点附近的应变硬化能力,应力比Rt2/Rt1、Rt5/Rt1均适宜用于表征X70级管线钢塑性阶段应变硬化能力,Rt2/Rt1较适宜用于表征X80级管线钢塑性阶段应变硬化能力.
关键词:
金属材料
,
铁素体/贝氏体多相钢
,
大变形管线钢
,
应变硬化行为
,
修正C-J分析
,
贝氏体体积分数
,
应力比
,
屈强比
HAN Enhou HAN KYumei ZHENG Yuli KE Wei Corrosion Science Laboratory
,
Institute of Corrosion and Protection of Metals
,
Academia Sinica
,
Shenyang
,
China postdoctoral
,
Institute of Corrosion and Protection of Metals
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
Based on theoretical analysis about local strain,strain rate and dissolving rate at crack tip, the corrosion fatigue crack growth rate of steels ZG20SiMn and SM50B-Zc in fresh water and 3.5% NaCl solution were measured experimentally,and the PH and electrode potential within crack were also measured continuously along with crack propagating.It showed that the increase of crack growth rate,caused by both decreasing frequency and raising stress ratio,was mainly accelerated by hydrogen embrittlement.
关键词:
corrosion fatigue
,
null
,
null
,
null
,
null
,
null
Daolun CHEN B.Weiss R.Stickler University of Vienna
,
Wahringer Street 42
,
A-1090 Vienna
,
AustriaZhongguang WANG State Key Laboratory for Fatigue and Fracture of Materials
,
Institute of Metal Research.Academia Sinica
,
Shenyang 110015
,
China
材料科学技术（英）
Near-threshold fatigue crack propagation behaviour of a cold-worked copper tested with distinct fa- tigue testing systems under different stress ratios has been investigated.The emphasis was placed on the evaluation of crack closure effect as well as the effective fatigue threshold,It was found that the fatigue threshold for R=0 is higher than those for R=-1 and R=0.4,for which almost the same threshold value was derived.Compared with the conventional closure evaluation method,the pro- posed new closure evaluation method can generally interpret the dependence of the fatigue thresh- old on stress ratio and loading condition,and leads to a higher and relatively constant effective fa- tigue threshold of about 3 MPa·m~(1/2) for the cold-worked copper at different stress ratios and loading conditions.
关键词:
near-threshold fatigue
,
null
,
null
钟警
,
贾敏
,
范春平
,
郑子樵
,
李红萍
,
吴秋萍
稀有金属材料与工程
研究取样方向、应力比以及微观组织对2050铝合金疲劳裂纹扩展速率的影响.结果表明:取样方向和应力比对疲劳裂纹扩展速率在近门槛区和快速扩展区的影响显著,而在稳态扩展区的影响则相对较小;L-T取样方向的速率最低,T-L取样方向的速率次之,S-L取样方向的速率最高,这主要与合金的晶粒取向、织构取向和第二相粒子取向有关;应力比为0.5的裂纹扩展速率高于应力比为0.1的速率,这在近门槛区主要与裂纹闭合效应有关,在快速扩展区主要受最大应力场强度因子Kmax的影响.
关键词:
2050铝合金
,
疲劳裂纹扩展速率
,
取样方向
,
应力比
,
微观组织
雒设计
,
赵康
,
王荣
机械工程材料
采用疲劳性能测试与回归分析相结合的方法,研究了S135钻杆钢在不同应力比下的疲劳裂纹扩展行为,获得了其在稳定扩展区和近门槛区的疲劳裂纹扩展速率表达式,并探讨了其疲劳断裂机制.结果表明:随着应力比R的增加,疲劳裂纹扩展速率曲线向左上方移动,da/dN增大,△Kth呈线性减小的趋势；近门槛区断口为解理断裂机制,稳定扩展区断口以疲劳条带扩展机制为主,同时也存在解理断裂.
关键词:
S135钻杆钢
,
疲劳裂纹扩展
,
应力比
,
断口
许天旱
,
冯耀荣
,
宋生印
,
金志浩
,
王党会
机械工程材料
利用电液伺服疲劳试验机及扫描电镜研究了应力比对J55钢疲劳裂纹扩展行为的影响.结果表明:在相同裂纹扩展长度处,随着应力比R的增大,疲劳裂纹扩展速率明显减小;在较低的△Keff区,应力比R对裂纹扩展速率的影响不显著,随着△Keff的升高,应力比对裂纹扩展速率的影响越来越显著;在相同的Kmax下,裂纹扩展速率随着应力比的增加而明显减小;随着应力比的增大,在高Kmax区,韧性断口的韧窝逐渐由抛物线状转变为等轴状.
关键词:
J55钢
,
应力比
,
疲劳裂纹扩展
,
应力强度因子幅值
许天旱
,
冯耀荣
,
宋生印
,
金志浩
,
王党会
钢铁研究学报
借助疲劳试验机及SEM,研究了应力比对J55钢级疲劳裂纹扩展性能的影响,并对断口形貌进行分析.结果表明:随着应力比增大,进入快速裂纹扩展区的△K变小,对于应力比0.1,低Paris区断裂模式为沿晶体学平面发生的穿晶断裂,Paris线性部分为由双滑移机制控制的疲劳条带断裂,高Paris区为疲劳条带断裂和延性静态断裂相结合的断裂模式;应力比为0.3、0.5与应力比为0.1的断裂模式相似;对于应力比0.7,沿晶体学平面发生穿晶断裂模式贯穿整个Paris区.
关键词:
J55钢级
,
疲劳裂纹扩展速率
,
应力比
,
断口形貌